Bonding Layer
Brand Code %Cr %Ti %Co %W %Al %Ni %Mo Cb+Ta %Fe Bond strength Hardness Usage BOUND 85 19 1 1 0.6 Bal 3 5.1 17 62 Mpa 30 HRC AS/FS BOUND 90 43 0.7 Bal 48 Mpa 30-35 HRC AS/FS BOUND 95 22 62.5 10 3.5 2 48 Mpa 92 HRC AS/FS BOUND 100 15 2.5 3.5 Bal 17 5.5 48 Mpa 35 HRC AS/FS BOUND 105 20 7 Bal 65 Mpa 85-95 HRC AS/FS BOUND 110 20 Bal 50 Mpa 90 HRC AS/FS BOUND 115 5.5 Bal 5 51 Mpa 75-85 HRC AS/FS BOUND120 5 Bal 54 Mpa 120 HB AS/FS BOUND 125 10 Bal 60 Mpa 128 HB AS/FS BOUND 130 20 Bal 63 Mpa 133 HB AS/FS -
Rebuilding Layer
Brand Code %C %Cr %Mn %Si %Al %Ni %Mo %Fe Bond Strength Hardness usage INOX 220 0.08 18 2.00 0.75 8.00 Bal 29 Mpa 190-210 HB AS INOX 425 0.80 0.70 0.30 Bal 33 Mpa 20-25 HRC AS INOX 435 0.04 1.5 2.30 0.10 4.50 1.30 90 27 Mpa 35 HRC AS INOX 440 23.5 0.45 1.00 5.30 Bal 43 Mpa 85-90 HB AS INOX 445 19 2.00 1.00 9.30 Bal 32 Mpa 95-100 HB AS INOX 446 0.30 13 1.00 1.00 Bal 42 Mpa 40-42 HRC AS INOX 450 0.08 17 2.00 1.00 12.00 2.50 Bal 42 Mpa 42-44 HRC AS INOX 455 0.15 0.80 0.20 Bal 39 Mpa 95-100 HB AS -
Hardfacing Layer
Brand Code %C %Cr %Mn %Si %Al %Ni %Mo %B %Nb %Cu %WC %TiC %Fe Bond Strength Hardness Usage HF 595 1.7 26 1.6 1.6 3 0.8 Bal 34 Mpa 39-42 HRC AS HF 596 5 28 1 1 Bal 34 Mpa 55-57 HRC AS HF 597 23 1.3 1 9 4 2.3 2 Bal 37 Mpa 45-50 HRC AS HF 698 27.5 1.7 1.6 3.7 Bal 41 Mpa 50-55 HRC AS HF 699 23 1 2 6 3.5 2.5 2 Bal 41 Mpa 50-55 HRC AS HF 700 13 1 6 2 26 6 Bal 37 Mpa 65 HRC AS HF 701 13.2 1.3 1.2 2 5.5 4.2 6 Bal 68 Mpa 67 HRC AS